| SAE |
SAE AMS4782 |
Nickel Alloy, Brazing Filler Metal, 71Ni - 10Si - 19Cr, 1975 °F (1080 °C) Solidus, 2075 °F (1135 °C) Liquidus |
|
| SAE |
SAE AMS4784 |
Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature, 50Au - 25Pd - 25Ni, 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range |
|
| SAE |
SAE AMS4787 |
Gold-Nickel Alloy, Brazing Filler Metal, High Temperature, 82Au - 18Ni, 1740 °F (949 °C) Solidus-Liquidus Temperature |
|
| SAE |
SAE AMS4785 |
Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature, 30Au - 34Pd - 36Ni, 2075 to 2130 °F (1135 to 1166 °C) Solidus-Liquidus Range_x000D_
|
|
| SAE |
SAE AMS4786 |
Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 70Au – 8.0Pd – 22Ni 1845 to 1915 °F (1007 to 1046 °C) Solidus-Liquidus Range_x000D_
_x000D_
|
|
| SAE |
SAE AMS4777 |
Nickel Alloy, Brazing Filler Metal, 82Ni - 4.5Si - 7.0Cr - 3.1B - 3.0Fe, 1780 °F (971 °C) Solidus to 1830 °F (999 °C) Liquidus Range |
|
| SAE |
SAE AMS4779 |
Nickel Alloy, Brazing Filler Metal, 94Ni - 3.5Si - 1.8B, 1800 °F (982 °C) Solidus, 1950 °F (1066 °C) Liquidus |
|
| SAE |
SAE AMS4776 |
Nickel Alloy, Brazing Filler Metal, 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon), 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus Range |
|
| SAE |
SAE AMS4775 |
Nickel Alloy, Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus |
|
| BSI |
BS A 315 |
Aerospace. Nuts, hexagonal, slotted (castellated), reduced height, normal across flats, with MJ threads, classifications: 450 MPa (at ambient temperature)/120anddeg;C, 450 MPa (at ambient temperature)/235anddeg;C, 600 MPa (at ambient temperature)/425anddeg;C, 900 MPa (at ambient temperature)/235anddeg;C, 900 MPa (at ambient temperature)/315anddeg;C, 900 MPa (at ambient temperature)/650anddeg;C, 1100 MPa (at ambient temperature)/235anddeg;C, 1100 MPa (at ambient temperature)/730anddeg;C and 1250 MPa (at ambient temperature)/60 |
|
| SAE |
SAE AMS4766 |
Silver Alloy, Brazing Filler Metal 85Ag - 15Mn 1760 to 1780 °F (960 to 971 °C) Solidus-Liquidus Range_x000D_
|
|
| BSI |
BS A 314 |
Aerospace. Nuts, hexagonal, plain, reduced height, normal across flats, with MJ threads, classifications: 450 MPa (at ambient temperature)/120 anddeg;C, 450 MPa (at ambient temperature)/235 anddeg;C, 600 MPa (at ambient temperature)/425 anddeg;C, 900 MPa (at ambient temperature)/235 anddeg;C, 900 MPa (at ambient temperature)/315 anddeg;C, 900 MPa (at ambient temperature)/650 anddeg;C, 1100 MPa (at ambient temperature)/235 anddeg;C, 1100 MPa (at ambient temperature)/730 anddeg;C and 1250 MPa (at ambient temperature)/ 600 anddeg;C. |
|
| SAE |
SAE AMS4773 |
Silver Alloy, Brazing Filler Metal, 60Ag - 30Cu - 10Sn, 1115 to 1325 °F (602 to 718 °C) Solidus-Liquidus Range |
|
| SAE |
SAE AMS4762 |
Silver Alloy, Brazing Filler Metal, 40Ag - 30Cu - 30Zn, 1245 to 1340 °F (674 to 727 °C) Solidus-Liquidus Range |
|
| SAE |
SAE AMS2663 |
Silver Alloy Brazing Filler Metal, 56Ag 22Cu 17Zn 5.0Sn, 1152 - 1203°F (622 - 651°C) Solidus-Liquidus Range |
|
| ISO |
ISO 9609 |
Aerospace - Nuts, hexagonal, plain, reduced height, normal across flats, with MJ threads, classifications: 450 MPa (at ambient temperature) /120 degrees C, 450 MPa (at ambient temperature) /235 degrees C, 600 MPa (at ambient temperature) /425 degrees C, 900 MPa (at ambient temperature) /235 degrees C, 900 MPa (at ambient temperature) /315 degrees C, 900 MPa (at ambient temperature) /650 degrees C, 1 100 MPa (at ambient temperature) /235 degrees C, 1 100 MPa (at ambient temperature) /730 degrees C and 1 250 MPa (at ambient temperature)/600 degrees C - Dimensions |
|
| ISO |
ISO 9618 |
Aerospace - Nuts, hexagonal, slotted (castellated), reduced height, normal across flats, with MJ threads, classifications: 450 MPa (at ambient temperature)/120 degrees C, 450 MPa (at ambient temperature)/235 degrees C, 600 MPa (at ambient temperature)/425 degrees C, 900 MPa (at ambient temperature)/235 degrees C, 900 MPa (at ambient temperature)/315 degrees C, 900 MPa (at ambient temperature)/650 degrees C, 1 100 MPa (at ambient temperature)/235 degrees C, 1 100 MPa (at ambient temperature)/730 degrees C and 1 250 MPa (at ambient temperature)/600 degrees C - Dimensions |
|
| ISO |
ISO 8279 |
Aerospace - Nuts, hexagonal, plain, normal height, normal across flats, with MJ threads, classifications: 600 MPa (at ambient temperature)/120 degrees C, 600 MPa (at ambient temperature)/235 degrees C, 900 MPa (at ambient temperature)/425 degrees C, 1 100 MPa (at ambient temperature)/235 degrees C, 1 100 MPa (at ambient temperature)/315 degrees C, 1 100 MPa (at ambient temperature)/650 degrees C, 1 210 MPa (at ambient temperature)/730 degrees C, 1 250 MPa (at ambient temperature)/235 degrees C and 1 550 MPa (at ambient temperature)/600 degrees C - Dimensions |
|
| ISO |
ISO 4147 |
Aerospace - Nuts, hexagonal, slotted (castellated), normal height, normal across flats, with MJ threads, classifications: 600 MPa (at ambient temperature)/120 degrees C, 600 MPa (at ambient temperature)/235 degrees C, 900 MPa (at ambient temperature)/425 degrees C, 1 100 MPa (at ambient temperature)/235 degrees C, 1 100 MPa (at ambient temperature)/315 degrees C, 1 100 MPa (at ambient temperature)/650 degrees C, 1 210 MPa (at ambient temperature)/730 degrees C, 1 250 MPa (at ambient temperature)/235 degrees C and 1 550 MPa (at ambient temperature)/600 degrees C - Dimensions |
|
| SAE |
SAE AMS4769 |
Silver Alloy, Brazing Filler Metal 45Ag - 24Cd - 16Zn - 15Cu 1125 to 1145 °F (607 to 618 °C) Solidus-Liquidus Range_x000D_
_x000D_
|
|
| SAE |
SAE AMS4765 |
Silver Alloy, Brazing Filler Metal 56Ag – 42Cu – 2.0Ni 1420 to 1640 °F (771 to 893 °C) Solidus-Liquidus Range_x000D_
|
|
| SAE |
SAE AMS4768 |
Silver Alloy, Brazing Filler Metal 35Ag - 26Cu - 21Zn - 18Cd 1125 to 1295 °F (607 to 702 °C) Solidus-Liquidus Range |
|
| SAE |
SAE AMS4763 |
Silver Alloy, Brazing Filler Metal, 56Ag - 22Cu - 17Zn - 5.0Sn, 1145 to 1205 °F (618 to 652 °C) Solidus-Liquidus Range_x000D_
|
|
| SAE |
SAE AMS4764 |
Copper Alloy, Brazing Filler Metal, 52.5Cu - 38Mn - 9.5Ni, 1615 to 1700 °F (879 to 927 °C) Solidus-Liquidus Range
|
|
| SAE |
SAE AMS4788 |
Silver Alloy Brazing Filler Metal 50Ag - 28Zn - 20Cu - 2.0Ni 1220 to 1305 °F (660 to 707 °C) Solidus-Liquidus Range_x000D_
_x000D_
|
|