ASTM A288-18(2023)

Standard Specification for Carbon and Alloy Steel Forgings for Magnetic Retaining Rings for Turbine Generators
Best Price Guarantee
Instant

$61.00

2-5 Days

$61.00

SAVE 10%

$109.80


Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


View in Library
or
...

1.1 This specification covers quenched and tempered carbon and alloy steel forgings for magnetic retaining rings for turbine generators.

1.2 Supplementary requirements of an optional nature are provided. These shall apply only when specified by the purchaser.

1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

This specification covers quenched and tempered carbon and alloy steel forgings for magnetic retaining rings for turbine generators. Specimens shall be manufactured by melting process and vacuum degassing. Forgings shall also undergo preliminary machining prior to heat treatment (quenching and tempering) for mechanical properties testing. Steel materials shall conform to tensile and notch toughness requirements, which include tensile strength, yield strength, elongation, reduction of area, and Charpy V-notch impact strength. Heat and product analyses shall be performed as well wherein specimens shall conform to chemical requirements of carbon, manganese, phosphorus, sulfur, nickel, chromium, molybdenum, and vanadium. Nondestructive tests such as magnetic particle test and ultrasonic inspection may also be performed.

SDO ASTM: ASTM International
Document Number A288
Publication Date March 15, 2023
Language en - English
Page Count 2
Revision Level 18(2023)
Supercedes
Committee A01.06
Loading...

Failed to load document history.

Publish Date Document Id Type View